Product description
Marlon Flow GF is an easy-flowing, cement and polymer-based ready mixed dry mortar product to which you only need to add water. Marlon Flow GF develops strength quickly and with its admixture has an extraordinary peel adhesion to the substrate. In hardened form, it is tension-free, corrosion-inhibiting and chloride resistant. Frost and weather resistant.
- Develops strength quickly
- Easy-flowing
- Polymer-modified
- Increased adhesion
- Tension-free
- Expands in the plastic phase
- Only requires added water
Marlon Flow GF is easy-flowing and is therefore well suited to the vertical cementing of metal items such as bolts, reinforcement rods, threaded rods etc. in concrete, brick and granite. The product can also be used for grouting and repair jobs.
In order to ensure the best possible adhe- sion to the surface/object, it must be clean of dust, oil, grease, cement slurry and other loose particles. Highly absorbent surfaces must be moistened to create a uniform, matt surface with low absorbency.
Marlon Flow GF is mixed with a low-speed drill with a two-blade mixing impeller attached. Cold mixing water is poured into a bowl/pail, after which the powder is added while continuing to stir the mixture. Mix thoroughly for at least 3 minutes until a lumpfree, easy-flowing consistency is achieved.
The ready-mixed mortar is used immediately after mixing. Marlon Flow GF should be used under normal circumstances at 20ºC within approximately 20 minutes. Keep stirring the mass throughout the entire cementing process. Lower temperatures extend and higher temperatures shorten the processing and hardening times.
Open surfaces should be protected against drying out too quickly where there are draughts, high temperatures and when exposed to sunlight with Marlon Curing B75. During the winter months, protect the mortar against extreme night frost, strong winds etc. (using winter mats, if necessary) during the first 24 hours of curing.
Casting should not take place in temperatures lower than +5°C. The product cannot tolerate frost during the curing and setting period.
Tools are cleaned with water immediately after use. Hardened Flow GF can only be removed mechanically.
Marlon Flow GF is subject to internal controls in accordance with Marlon’s quality assurance system. Subsequent measuring and mixing at the site of application is not included in the quality control.
Manufacturer
Marlon Tørmørtel A/S
Virkelyst 20
8740 Brædstrup
Material type
Cement based grouting and anchoring mortar.
Filler material
Oven-dried and sorted silica sand (Dmax) 0.5 mm.
Additives
Polymer, plasticising and stabilising additives.
Added water
19-21 % of dry powder weight (3.4-3.8 l per 18 kg).
Yield
10 l liquid mortar per 18 kg/sack.
Layer thickness
2-30 mm. Guideline.
Cement type
Portland cement. CEM I 52,5 N (LA).
Application time
Approx. 20-30 minutes.
Storage
Min. 12 months in dry and suitable conditions in unopened packaging.
Packaging
18 kg plastic sack.
| Technical data | Value | Method |
| Compressive strength, 1 day | > 20 MPa | DS/EN 12190 |
| Compressive strength, 7 days | > 45 MPa | DS/EN 12190 |
| Compressive strength, 28 days | > 55 MPa | DS/EN 12190 |
| Bending tensile strength, 7 days | > 8 MPa | DS/EN 12190 |
| Bending tensile strength, 28 days | > 10 MPa | DS/EN 12190 |
| Air content | 1-3% | DS/EN 1015-7 |
| Density | 2111 kg/m3 | DS/EN 1015-7 |
| Chloride content | < 0,01 weight% | |
| Chromate content | < 2 mg/kg cement | DS/EN 1015-17 |
| Information | ||
| Item no. | 10539 | |
| Pr no. | 4298183 | |
| DB-no. | Application pending | |
| Version | 07.18 erst. - |
|
|
Marlon Tørmørtel A/S Virkelyst 20 8740 Brædstrup År 18 DoP 1000539 |
EN 1504-3 1073-CPR-171-01 Concrete repair product for construction repairs. CC mortar, based on hydraulic cement. |
| Compressive strength | > 45 MPa class R4 |
| Chloride content | ≤ 0,05% |
| Adhesion | ≥ 2,0 MPa |
| Carbonatization | Passed |
| Elastic modulus | ≥ 20 GPa |
| Thermal compatibility | Del 1 ≥ 2,0 MPa |
| Capillary absorption | ≤ 0,5 kg x m-2 x h-0,5 |
| Hazardous substances | In accordance with section 5.4 |
| Fire-resistance | Class A1 |
|
|
Marlon Tørmørtel A/S Virkelyst 20 8740 Brædstrup År 18 DoP 1000539 |
EN 1504-6 1073-CPR-171-03 Concrete repair product for the anchoring of reinforcement rods. |
| Tensile strength | Moving < 0,6 mm at a load of 75 MPa |
| Chloride content | ≤ 0,05% |