A solid solution
Grout EKF 602LM

High flow mortar

Grout EKF 602LM

Expanding liquid mortar for grouting jobs

Produktbeskrivelse

Marlon Grout EKF 602LM is a factory-produced expanding liquid mortar made of Portland cement, mineral adhesives, additives, latex polymer and oven-dried silica sand with a controlled grain curve. The product’s high content of latex polymer gives the mortar particularly good flow and adhesive properties. Marlon Grout EKF 602LM requires only the addition of water and, when mixed, is a very fluid pumpable mortar. For large projects, the mortar can be applied with the help of a suitable screw or piston pump. The product satisfies the material requirements for the extra aggressive environmental class E (see DS/EN 206 DK NA:2020).

Benefits
  • Pumpable expanding liquid mortar
  • Shrinkage-compensated
  • Latex-modified
  • High strength
  • Just add water
Applications

Marlon Grout EKF 602LM is used, e.g. for grouting of machine foundations and embedment work. Marlon Grout EKF 602LM is also well suited for jointing underneath and between prefabricated concrete elements, for pouring of corrugated pipes in concrete element constructions or for projects that are difficult to access with traditional methods.

Pre-treatment

To ensure the best possible adhesion for existing concrete, the surface must be cleaned of any cement slurry, oil, grease or other loose impurities through, e.g. chipping, sandblasting or high-pressure cleaning, and reinforcing iron must be cleaned of rust and chlorides. The cleaned surface must be watered, to produce a uniform, dull and slightly absorbent surface. Metal surfaces must be cleaned of any grease, rust etc.

Mixing

Marlon Grout EFK 602LM is mixed with clean water (approx. 13-14 weight percentage). The dry powder and approx. 80% of the water for mixing is poured into a suitable agitator mixer. During effective mixing, the remaining water is added until you achieve a very fluid, lump-free mortar. Manual mixing can be done in a tub/bucket using a drill with a two-bladed propeller mixer. When mixing with a drill, first pour the water into the bucket, and then add the powder while mixing. Mix until you achieve a very liquid consistency. The mixing time should be at least 3 min. On mixing and application, check that the compound does not separate.

Application

Marlon Grout EFK 602LM can generally be applied in thicknesses from approx. 5 mm up to 60 mm. For greater layer thicknesses, an aggregate of larger stone fractions of 20-25% can be added. Depending on the nature of the surface, large variations in the surface can result in contraction cracks. To achieve optimal benefit from the expansion, blend only the amount of mortar that can be used within approx. 20 min at +20°C. Higher temperatures will shorten, and higher temperatures will lengthen both the processing and hardening times.

Aftercare

The newly poured mortar surface must not be exposed to loads and must be protected as quickly as possible after pouring against rapid drying from draughts, high room temperature, sun rays, etc. Use of sealed plastic or a suitable curing membrane is recommended.

Limitations

Marlon Grout EKF602LM should not be used at temperatures under +5°C or over +30°C. The product does not tolerate frost during the curing and cementation period.

Cleaning

Clean tools with water immediately after use. Hardened Grout EKF 602LM can only be removed mechanically

Inspection

Marlon Grout EKF 602LM is subject to internal inspection according to Marlon’s quality assurance system. Subsequent measuring and mixing at the site of application is not included in quality control.

Teknisk information

Manufacturer
Marlon Tørmørtel A/S
Virkelyst 20
DK-8740 Brædstrup

Material type
Cement-based, expanding concrete.

Environmental class
Extra aggressive.

Added water
13-14 % of the dry powder weight. (3.5 l per 25 kg) v/c < 0.40.

Yield
Approx. 13 l per 25 kg.

Opening time
Approx. 30 min., depending on temperature.

Layer thickness
Approx. 5-80 mm. Guideline.

Consumption
Approx. 2 kg dry powder product per m² per mm layer thickness.

Adhesive agent
Portland cement. CEM I 52.5 N (LA).

Filler material
Oven-dried and sorted silica sand, cl. E.

Additives
Plasticiser, expanding and stabilising additives.

Packaging
25 kg plastic sacks or big bags.

Storage
The storage life is min. 12 months in dry and suited conditions in unopened packaging.

Technical data Values Method
Compressive strength, 1 day > 20 MPa DS/EN 12190
Compressive strength, 3 days > 40 MPa DS/EN 12190
Compressive strength, 7 days > 50 MPa DS/EN 12190
Compressive strength, 28 days > 60 MPa DS/EN 12190
Bending tensile strength, 7 days > 8 MPa DS/EN 12190
Bending tensile strength, 28 days > 10 MPa DS/EN 12190
Air content Approx. 3 % DS/EN 1015-7
Consistency > 200 mm DS/EN 1015-3
Expansion of fresh mortar 0.4-0.6 %  
pH value Approx. 12.5 for fresh mortar  
Chromate content < 2 mg/kg cement  

 


 

Information    
Item no. 10505  
Pr no. 2377734  
DB no. 1461128  
Version 07.14 replaces 11.12  

 


 

Marlon Tørmørtel A/S
Virkelyst 20
8740 Brædstrup
Year 12
DoP 1000505
EN 1504-3
1073-CPR-171-01
Concrete repair product for construction repairs. CC mortar, based on hydraulic cement.

 


 

Compressive strength > 45 MPa class R4
Chloride content ≤ 0,05 %
Adhesion ≥ 2.0 MPa
Frost/thaw ≥ 2.0 MPa
Carbonatization Passed
Elastic modulus ≥ 20 GPa
Thermal compatibility Part 1 ≥ 2,0 MPa
Capillary absorption ≤ 0.5 kg x m-2 x h-5
Hazardous substances In accordance with section 5.4
Fire-resistance Class A1